High Alumina Refractory Castable Refractory Cement for Rotary Cement Kiln

• Customization: Available
• Feature: Long Time Materials
• Refractoriness (℃): 1580< Refractoriness< 1770
• Shape: Powder
• Type: Refractory Material
• Material: Castable
• Transport Package: 25kg Bag
• Trademark: JI Steel
• Origin: Henan, China
• Production Capacity: 100000 Mt / Year

Product Description

Product Description

 

High Alumina Refractory Castable Refractory Cement for Rotary Cement Kiln

 

Self-flowing refractory castables are used in narrow parts of the kiln lining, or when various kilns are repaired and damaged. The characteristics of self-flowing refractory castables are high-temperature hot self-flowing pouring.

High-alumina self-flowing refractory castables are based on high-strength low-cement castables with self-flowing agents, anti-explosion agents and a certain amount of mineralizers. There is no need for forming vibration during construction, which can reduce noise, improve the environment and reduce labor intensity. And it has the characteristics of high strength, good toughness, high refractoriness, good fluidity, strong resistance to peeling and wear resistance, and convenient construction.

High-aluminum self-flowing refractory castables are generally in the mixing equipment, and the wet mixing time is about 6 minutes. Although corundum fine powder affects the flow performance of the self-flowing material, it can improve the refractory performance of the matrix in the self-flowing castable, and can be added appropriately. It is not easy to add too much or too little ultra-fine powder in the high-alumina self-flowing castable. The general addition is 7%~9%. The water reducing agent needs to be added separately, which can improve the flow performance and mechanical properties of the high-alumina self-flowing castable , the amount added should be controlled within the range.
 

Product Parameters

Self-flow High Alumina Refractory Castable
1	Long Time Working Temp.		1350ºC
2	Refractoriness		>=1770ºC
3	Bulk Density after drying at 110ºC*24h		>=2.45g/cm^3
4	Mould of Rupture	After drying at 110ºC*24h	>=6 Mpa
		After firing at 1350ºC*3h	>=8 Mpa
5	Cold Crushing Strength	After drying at 110ºC*24h	>=45 Mpa
		After firing at 1350ºC*3h	>=60 Mpa
6	Permanent Linear Change	After drying at 110ºC*24h	±0.2%
		After firing at 1350ºC*3h	±0.5%
7	Al2O3%		>=60%

 

Detailed Photos

Our Advantages

1. The technical team of more than 20 people provides customers with professional and cost-effective design solutions.
2. Each process has a special quality supervisor to strictly control the quality.
3. Perfect and timely after-sales service system, 24-hour response to customer needs, worry-free after-sales.

Company Profile

Founded in 2004, JI Steel has 20 years of professional experience in the metallurgical industry and is committed to the design, production, research and development of materials in the metallurgical and steel industry, and provides a series of high-quality, innovative and cost-effective products and solutions for steel mills. The main products include copper mould tubes, graphite electrodes, refractories for steel-melting and continuous casting.

JI Steel has 3 factories, nearly 10,000 employees, and an independent scientific research and technical team of 50 people with rich experience in the metallurgical and steel-making industries. It can provide customers with customization, design, construction, installation, maintenance, replacement, and technical consultation. and other services. JI Steel has advanced CNC machining center, advanced production technology, advanced water treatment system, and strictly controls zero discharge in accordance with environmental protection requirements to build a green and environmentally friendly enterprise.

Our products are recognized by SGS, OMIC, IKA, ISQI, COTECNA and other well-known international inspection agencies, and our products are exported to Europe, Asia, Africa, South America, the Middle East and other countries, enjoying a good reputation.

Packaging & Shipping